| [Mo2O4]2+交联层柱粘土的制备及其结构和性能的研究 |
| THE STUDIES ON THE PREPARATION, STRUCTUREAND PROPERTIES OF [Mo2O4 ]2+ CROSS-LINKED PILLARED CLAY |
|
| 摘要: 以[Mo2O4]2+溶液为交联剂制备了钼交联层柱粘土。并用XRD、IR、LRS、XPS及TPD等手段对其结构及Mo的存在状态进行了研究。结果表明:[Mo2O4]2+被交换进入了层间,所得层柱粘土的d001～13Å,其柱结构为MoxOy的簇状氧化物。当交联剂在粘土层间的量超过粘土的交换容量时,Mo在层外表面偏析。酸性研究显示:Mo的加入使钼交联层柱粘土的酸中心数较之原土增加,并以Lewis酸为主。用异丙醇脱水和氧化反应考察钼交联层柱粘土的催化活性,结果表明,这种层柱粘土不仅具有酸催化活性,同时由于钼的引入而具有氧化活性和抗积炭性能。 |
| 关键词: 钼双核聚离子 交联 层柱 粘土 催化 |
| 基金项目: 石油化工科学研究院资助 |
| Abstract: Mo Cross-linked pillared Clay (Mo-PC) has been prepared with [Mo2O4]2+ aquated solution as cross linking agent. The structure and properties of the prepared Mo-PC were studied by XRD,IR,LRS,XPS and TPD methods.The results show that Mo can be exchanged into interlayer,the Mo-PC has the basal spacing d001～13Å and the pillar structure is MoxOy clusters which are so symmerical that Mo-PC has no activity in LRS. It is found that MoxOy become pillars when Mo wt.% ≤ 3.96 and will be segregated out of interlayer onto the surface when Mo wt.%>3.96.The acidity of Mo-PC were studied by IR and NH3-TPD. Mo-PC has more acid sites than Ca-montmorillonite due to having Mo. The acid sites are mainly Lewis type.The dehydrogenation and dehydration of isopropanol were chosen as a probe to test the catalytic properties of the catalysts prepared. The results indicate that Mo PC has higher dehydration activity than Ca-montmorillonite and also has dehydrogenation activity for having Mo.No coking reaction was detected on the Mo-PC. |
| Keywords: dinucieus Mo anion cross-linked pillared clay catalysis |
| 投稿时间：1988-11-30 |
| 摘要点击次数: 1264 |
| 全文下载次数: 1607 |
| 毛辉,金永漱,陈懿.[Mo2O4]2+交联层柱粘土的制备及其结构和性能的研究[J].无机化学学报,1989,5(2):8-15. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|