| EDTA-凝胶法制备PLZT超微粉的研究 |
| STUDIES ON PREPARATION OF PLZT ULTRAFINE PARTICLES BY THE EDTA-GEL METHOD |
|
| 摘要: 以金属的硝酸盐和EDTA为原料,用EDTA-凝胶法制备均匀性好的PLZT超微粉。经FT-IR光谱、热重和差热分析、X射线衍射分析和透射电镜等方法研究表明：硝酸根离子可以加速EDTA-凝胶的热分解,仅在250℃时便有PLZT相生成,除PbO外不出现其他中间相,经600℃煅烧所得到的单一PLZT相超微粉,平均粒径为35nm。 |
| 关键词: 锆钛酸铅镧(PLZT) EDTA-凝胶 超微粉 |
| 基金项目: 国家自然科学基金资助项目 |
| Abstract: Using nitrates and EDTA as raw materials, high homogenous, superfine powders of PLZT have been prepared by the EDTA-gel method. The results of FI-IR spectra, DTA-TG, XRD and TEM show that nitrate ions accelerate the decomposition of the EDTA-gel.The main products are PLZT powders in which there is no other interphases besides PbO phase at 250℃.The superfine powders of monophase PLZT have been produced after calci-nation at 600℃ and the average size is about 35 nm. |
| Keywords: lead lathanum zirconate titanate(PLZT) EDTA-gel ultrafine powder |
| 投稿时间：1995-09-04 |
| 摘要点击次数: 1064 |
| 全文下载次数: 1477 |
| 方佑龄,赵文宽,张蕾.EDTA-凝胶法制备PLZT超微粉的研究[J].无机化学学报,1996,12(3):267-271. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|