| 过氧化合物法PLZT纳米粉体的制备和表征 |
| Preparation and Characterization of Nanosized Powder PLZT by Peroxide Method |
|
| 摘要: |
| 关键词: 锆钛酸铅镧(PLZT) 过氧化合物前驱体 纳米粉体 |
| 基金项目: 国家自然科学基金资助项目(No.20073030) |
| Abstract: Pb0.92La0.08(Zr0.65Ti0.35)0.98O3 (PLZT) nanosized powder was prepared from the corresponding nitrate alnd H2O2 by thermal decomposition of the peroxide.FT-IR, DTA-TG, XRD, TEM, and chemical analyses indicated that: (l) Peroxide precursor of PLZTwas composed of Pb0.92La0.08(Zr0.65Ti0.35)0.98O2(O2)·3H2O; (2) PLZT started to form at 550℃, but PbO and PbZrO3 still existed; (3) homogeneous tetragonal crystals of PLZTwere formed at 700℃, with average particle diameter of 22nm; (4) the sizes of the crystals increased with increasing calcination temperatures, crystals of PLZTwere formed at 850℃ with average particle diameter of 56nm. |
| Keywords: lead lanthanum zirconate titanate(PLZT) peroxide precursor nanosized powders |
| 投稿时间：2000-10-11 修订日期：2000-11-27 |
| 摘要点击次数: 1034 |
| 全文下载次数: 1012 |
| 赵文宽,方佑龄.过氧化合物法PLZT纳米粉体的制备和表征[J].无机化学学报,2001,17(2):292-296. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|