| SiO2载体表面原位合成MCM-41的结构特征 |
| Structural Characteristics of MCM-41 Synthesized in-situ on Silica |
|
| 摘要: 以溶液硅源和表面硅源两种合成路线在SiO2颗粒表面进行了MCM-41的原位合成,结果发现以两种方式均可得到MCM-41的有序结构。溶液硅源原位合成MCM-41的长程结构较好,两种硅源原位合成的MCM-41均能够在脱除模板剂过程中保持其长程有序结构。表面硅源原位合成MCM-41的孔径分布较窄,最可几孔径为3.81nm。本文还考察了OH/CTABr及SiO2/OH比对表面硅源原位合成MCM-41长程结构特征的影响。 |
| 关键词: MCM-41 原位合成 SiO2载体表面 |
| 基金项目: |
| Abstract: MCM-41 has been synthesized in-situ on silica both using solution silicate and surface silicate as Si sources. The long-range structure of MCM-41 synthesized with solution silicate as Si source is better than that of MCM-41 with surface silicate as Si source, while either is as stable as to preserve the long-range ordered structure during calcination. For the MCM-41 sample synthesized with surface silicate as Si source, the pore diameters are narrowly distributed with approximately 3.81nm in the maximum distribution. |
| Keywords: MCM-41 in-situ synthesis silica support surface |
| |
| 摘要点击次数: 1351 |
| 全文下载次数: 1277 |
| 何静,段雪,李成岳,朱月香.SiO2载体表面原位合成MCM-41的结构特征[J].无机化学学报,2002,18(2):161-165. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|