| LiCoO2梯度包覆LiNi0.96Co0.04O2电极材料的电化学性能 |
| Electrochemical Performance of LiCoO2 Gradient Coated LiNi0.96Co0.04O2 Cathode |
|
| 摘要: |
| 关键词: LiNiO2 LiCoO2 梯度包覆 正极材料 |
| 基金项目: |
| Abstract: LiCoO2 gradient coated LiNi0.96Co0.04O2 material and iso-structure LiNi0.8Co0.2O2 material (the same molar ratio 8/2 of Ni/Co in the two materials) as cathode for lithium-ion batteries were synthesized with a co-precipitation method. Microstructure of iso-structure LiNi0.8Co0.2O2 were about the same as that of LiNiO2, and the structure of the coated material was much more similar to that of LiCoO2 based on the X-ray diffraction patterns. The cycling voltammetry and galvanostatic cycle tests show that the properties of the coated material were improved significantly. The first specific charge and discharge capacity for the coated material was 249.20 mAh·g-1 and 207.90 mAh·g-1 respectively, and the specific discharge capacity for the 100th cycle was still 186.02 mAh·g-1 with an irreversible loss of only 21.1 mAh·g-1.This showed that the new material had a good lithium intercalation-deintrercalation performance. Meanwhile, the mechanism of the sintering reaction was proposed. During the sintering reaction of the precursor with LiOH, the Li+-ion permeated into the body of precursors because the shape of the precursor particles was not changed basically based on scanning electronic microscopy. So, the layer microstructure of the precursor is important for the layer microstructure of lithium nickel cobalt oxides electrode material. |
| Keywords: LiNiO2 LiCoO2 gradient coated cathode |
| 投稿时间：2004-09-06 修订日期：2005-01-20 |
| 摘要点击次数: 1227 |
| 全文下载次数: 1643 |
| 顾大明,史鹏飞,宋振业,张鼎.LiCoO2梯度包覆LiNi0.96Co0.04O2电极材料的电化学性能[J].无机化学学报,2005,21(5):725-728. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|