| 室温快速合成SnSe纳米棒 |
| A Rapid, Room Temperature Route to SnSe Nanorods |
|
| 摘要: |
| 关键词: SnSe纳米棒 柠檬酸 |
| 基金项目: |
| Abstract: The synthesis of crystalline SnSe nanorods was successfully achieved via a chemical reaction between sodium selenosulfate (Na2SeSO3) and SnCl2·2H2O in alkaline aqueous solution in the presence of the complexing agent (trisodium citrate) at room temperature under ambient air. The product was characterized by X-ray diffraction (XRD), transmission electron microscopoy (TEM) and X-ray photoelectron spectroscopy (XPS). The results reveal that the SnSe nanorods are well crystalline with an average diameter of 85 nm and the lengths up to 10 μm. The possible mechanism for the formation of SnSe is also discussed. |
| Keywords: SnSe nanorods trisodium citrate |
| 投稿时间：2005-04-11 修订日期：2005-07-01 |
| 摘要点击次数: 2052 |
| 全文下载次数: 2452 |
| 韩巧凤,祝艳,刘孝恒,杨绪杰,陆路德,汪信.室温快速合成SnSe纳米棒[J].无机化学学报,2005,21(11):1740-1742. |