层状Co3O4的制备及其电化学电容行为 |
Preparation and Electrochemical Capacitance of Layered Co3O4 |
|
摘要: 以P123为模板水热合成制备了Co2(OH)2CO3前驱体,200 ℃热处理后得到了具有层状结构的Co3O4。循环伏安、恒流放电等电化学测试表明,200 ℃所得Co3O4电极在6 mol·L-1 KOH溶液中和-0.1~0.5 V(vs Ag/AgCl)电位范围内,具有较好的循环稳定性能,单电极比电容达到505 F·g-1。 |
关键词: 层状Co3O4 超级电容器 电容性能 |
基金项目: |
Abstract: A layered Co3O4 was obtained by thermal decomposition of Co2(OH)2CO3 precursor prepared via a hydrothermal process. The structure and morphology were examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Electrochemical properties of Co3O4 electrode were preformed by cyclic voltammogram and galvanostatic charge/discharge measurements in 6 mol·L-1 KOH electrolyte with the potential range from -0.1 to 0.5 V (vs Ag/AgCl). The results demonstrated that the layered Co3O4 obtained at 200 ℃ had a good stability and cyclic performance. Its specific capacitance as single electrode was up to 505 F·g-1. |
Keywords: Co3O4 supercapacitor capacitance |
|
摘要点击次数: 1080 |
全文下载次数: 1827 |
王兴磊,何宽新,张校刚.层状Co3O4的制备及其电化学电容行为[J].无机化学学报,2006,22(6):1019-1022. |
查看全文 查看/发表评论 下载PDF阅读器 |
Support information: |
|
|
|