ZnO-B2O3∶Tb3+长余辉玻璃的发光性质 |
Long-lasting Luminescence Properties of ZnO-B2O3∶Tb3+ |
|
摘要: 通过还原方法制备了Tb3+离子掺杂的硼酸锌玻璃,并观察到在254 nm紫外光激发后有明亮的绿色长余辉发光现象,余辉时间达6 h。通过激发与发射光谱、余辉光谱、余辉衰减曲线、热释光谱、热释光释出速率衰减曲线等得到的信息,研究了Tb3+离子掺杂的硼酸锌玻璃的发光性质。 |
关键词: 长余辉发光 铽 硼酸锌玻璃 |
基金项目: |
Abstract: Tb3+ activated ZnO-B2O3 glass shows bright and long-lasting phosphorescence (LLP). After irradiation by 254 nm light, a visible greenish light with dominating peak at 542 nm can be observed with naked eyes in the dark for up to 6 h after removal of the activating light. The thermoluminescence spectra of Tb3+-doped glasses illuminated by UV light at room temperature consist of two dominant components with the 382 K peak related to the LLP phenomena. Electron spin resonance (ESR) measurements show that electron trapping centers and hole trapping centers are formed by UV irradiation and their intensity decays slowly in both Tb3+-free and Tb3+-doped glasses. Based on these facts, we suggest that long-lasting phosphorescence is related closely to this UV induced electron and hole traps that serve effectively as electron donor and accepter, and that these defects are controlled by the composition and structure of the glasses. |
Keywords: long-lasting luminescence Tb3+ zinc borate glass |
|
摘要点击次数: 1295 |
全文下载次数: 1285 |
廉志红,王静,王淑彬,苏锵.ZnO-B2O3∶Tb3+长余辉玻璃的发光性质[J].无机化学学报,2006,22(9):1640-1644. |
查看全文 查看/发表评论 下载PDF阅读器 |
Support information: |
|
|
|