| 锂离子电池用SnO2-聚苯胺复合负极材料的制备与表征 | |
| Synthesis and Characterization of SnO2-polyaniline Composite as Anode for Lithium Ion Batteries | |
| 摘要: 以苯胺、过硫酸铵和SnO2为原料通过微乳液聚合法合成了SnO2-聚苯胺的复合材料，并通过X-射线衍射、红外吸收光谱、扫描电镜和电化学测试等手段对所得复合材料进行了表征与分析。结果表明，复合材料中的聚苯胺是无定形的，聚苯胺在反应过程中沉积在SnO2颗粒上形成SnO2被聚苯胺包裹的复合材料。电化学测试说明，该复合材料的首次容量达到657.6 mAh·g-1，经过80次循环后每次循环的容量衰减率仅为0.092%。 | |
| 关键词: SnO2 聚苯胺 锂离子电池 微乳液聚合法 | |
| 基金项目: | |
| Abstract: The SnO2-polyaniline (SnO2-PAn) composite was prepared by microemulsion polymerization method using aniline, ammonium peroxodisulfate and SnO2 as starting materials. The SnO2-PAn was confirmed by IR, XRD, SEM and electrochemical tests.Results show that PAn in the composites is amorphous. The PAn formed in the reaction is deposited preferentially on the SnO2 particles giving a SnO2-PAn composite，in which the SnO2 is coated with the PAn. SnO2-PAn composite shares reversible capacity of 657.6 mAh·g-1 and the capacity loss per cycle is only 0.092% after 80 cycles. | |
| Keywords: SnO2 polyaniline lithium ion battery microemulsion polymerization method | |
| 摘要点击次数: 992 | |
| 全文下载次数: 1097 | |
| 何则强,刘文萍,熊利芝,舒晖,吴显明,陈上,黄可龙.锂离子电池用SnO2-聚苯胺复合负极材料的制备与表征[J].无机化学学报,2007,23(5):813-816. | |