| Na0.33WO3溶胶及薄膜的制备与光致变色性质研究 | |
| Synthesis and Photochromism Property of Colloidal and Films of Tungsten Bronze | |
| 摘要: | |
| 关键词: 钨青铜 水热合成 光致变色 薄膜 | |
| 基金项目: | |
| Abstract: Under hydrothermal conditions, the colloidal of Na0.33WO3 were obtained by using Na2WO4·2H2O as the starting material. The products were characterized by XRD, XPS, ICP and IR methods. The color of Na0.33WO3 sol can easily change from purple to blue-purple, then to blue by UV irradiation with good reversibility. There are three absorbance peaks in UV-Vis-NIR transmission spectra of the Na0.33WO3 sol mixed with trace PVA. The XPS measurement shows that the number of W5+ increased after UV irradiation. The PVA/NaxWO3 thin films were deposited on quartz substrates by dip-coating technique with the mixture of PVA, Na0.33WO3 sol and water. The photochromic property of the film was studied. | |
| Keywords: tungsten oxide bronze hydrothermol synthesis photochromic property film | |
| 摘要点击次数: 1075 | |
| 全文下载次数: 2011 | |
| 徐英明,霍丽华,程晓丽,赵辉,高山.Na0.33WO3溶胶及薄膜的制备与光致变色性质研究[J].无机化学学报,2007,23(5):867-870. | |
| 查看全文 查看/发表评论 下载PDF阅读器 | |
| Support information: | |
|
| |
|
| |
|
| |