| 沉淀法制备不同形貌和结构的纳米BiVO4 | |
| Synthesis of Different Morphologies and Structures of Nano-sized BiVO4 by Precipitation Method | |
| 摘要: 采用液相沉淀法，通过选择不同起始原料并控制反应温度和pH值，制备得到不同形貌和结构的纳米BiVO4。采用X-射线衍射(XRD)、透射电子显微镜(TEM)和紫外-可见吸收光谱(UV-Vis)技术对产物进行分析表征。结果表明，采用NH4VO3作V源，室温下可直接制备得到结晶好的四方晶系硅酸锆型BiVO4球形纳米颗粒，提高反应液pH值或升高温度，可得到单斜晶系白钨矿型BiVO4，采用NaVO3作为V源，室温下可直接得到单斜晶系白钨矿型片状BiVO4。加入不同类型表面活性剂则得到不同形貌的BiVO4。 | |
| 关键词: 钒酸铋 沉淀法 纳米 形貌 | |
| 基金项目: | |
| Abstract: The nano-sized BiVO4 with different morphologies and structures was synthesized by precipitation method through choosing different raw materials and controlling the reaction temperature and pH value. X-ray Diffraction (XRD), Transmission Electron Microscope (TEM) and UV-Vis absorbance spectroscopy were used to characterize the products. The results showed that highly crystalline tetragonal zircon-type structure of nano-sized BiVO4 with spherical particles was obtained at room temperature using NH4VO3 as the reactant. Monoclinic scheelite structure of BiVO4 was obtained through increasing the reaction temperature or the pH value. By choosing NaVO3 as the raw materials, monoclinic scheelite structure BiVO4 with a plate or rod-like shape was obtained directly at room temperature. BiVO4 with different morphologies was obtained when using different surfactants. | |
| Keywords: BiVO4 precipitation method nano-sized morphologies | |
| 摘要点击次数: 1497 | |
| 全文下载次数: 1821 | |
| 高善民,乔青安,赵培培,陶芙蓉,张江,戴瑛,黄柏标.沉淀法制备不同形貌和结构的纳米BiVO4[J].无机化学学报,2007,23(7):1153-1158. | |
| 查看全文 查看/发表评论 下载PDF阅读器 | |
| Support information: | |
|
| |
|
| |
|
| |