| 化学浴沉积法制备高取向钒酸铋薄膜 |
| Preparation of Oriented BiVO4 Thin Film by Chemical Bath Deposition |
|
| 摘要: |
| 关键词: 钒酸铋(BiVO4)薄膜 化学浴沉积 择优取向 |
| 基金项目: |
| Abstract: Highly oriented BiVO4 films were synthesized on glass substrates by modified chemical bath deposition (CBD). The influence of the deposition parameters as temperature and time of deposition on the rate of process and the quality of BiVO4 films was studied by XRD, Raman Spectroscopy and SEM. The film deposited at 90 ℃ for 12 h was dense and uniform. The BiVO4 thin film under this optimal depositing conditions was consisted of octagonal crystalline grains in a narrow size distribution with an average size of about 7 μm, showing a (004) preferential orientation. |
| Keywords: BiVO4 film chemical bath deposition orientation |
| |
| 摘要点击次数: 1683 |
| 全文下载次数: 2016 |
| 刘晶冰,汪浩,张慧明,张文熊,严辉.化学浴沉积法制备高取向钒酸铋薄膜[J].无机化学学报,2007,23(7):1299-1302. |