| Ag/C同轴纳米电缆的制备 |
| Fabrication of Ag/C Coaxial Nanocables |
|
| 摘要: 采用十六烷基三甲基溴化铵(CTAB)辅助水热法合成了Ag/C同轴纳米电缆，并用SEM、TEM、XRD和EDS对产物进行了表征。结果表明，产物为长达数十微米，内核直径80～100 nm，壳厚约100 nm的纳米电缆。初步探讨了Ag/C同轴纳米电缆的生长机制。 |
| 关键词: 水热 Ag 纳米电缆 |
| 基金项目: |
| Abstract: Ag/C coaxial nanocables were fabricated by a hydrothermal method in the presence of cetyltrimethylammonium bromide(CTAB). The as-synthesized Ag/C coaxial nanocables were characterized by SEM, TEM, XRD and EDS. The results show that products are coaxial nanocables with lengths of several tens microns, core about 80～100 nm in diameter, and a surrounding sheath about 100 nm in thickness. The formation process of Ag/C coaxial nanocables was proposed. |
| Keywords: hydrothermal Ag nanocables |
| |