| 发光材料BaAl2Si2O8∶Eu2+的物相结构与发光性能 |
| Phase Structure and Luminescence Properties of BaAl2Si2O8∶Eu2+ Phosphor |
|
| 摘要: |
| 关键词: 钡长石 发光 Eu2+ 光谱性质 |
| 基金项目: |
| Abstract: A phosphor, Ba0.97Al2Si2O8∶Eu2+, was synthesized by high temperature solid-phase method at different temperatures. The samples were characterized by TG/DTA, XRD and fluorescence spectroscopy. The results show that the main phase for host of these luminescence materials is barium feldspar BaAl2Si2O8∶Eu2+ and there is a transition from hexagonal crystal system to monoclinic crystal system in the process of the sintering of barium feldspar. The luminescent phenomen of barium feldspar with hexagonal structure can not be observed under the excitation of ultraviolet lamp of 365 nm while the barium feldspar with monoclinic structure has excellent luminescence properties. The excitation spectra of all these samples show broad band spectra ranging from 250～390 nm with peak at λex of 357 nm，which indicates that these samples can be effectively excited by near ultraviolet ; the emission spectra range from 380～600 nm with peak at λem of 433 nm. The luminescent intensity increases then decreases with the concentration of doping Eu2+ ions. When the concentration of dopants is 2.5mol%, the luminescent intensity reaches the maximum value. When the concentration of Eu2+ ions changes from 0.5mol% to 2.5mol%, the emission peak has a red shift from 427 nm to 440 nm. |
| Keywords: barium feldspar luminescence Eu2+ spectrum properties |
| |
| 摘要点击次数: 1125 |
| 全文下载次数: 1953 |
| 柏朝晖,龚兵勇,田一光,张 乔,宋 超.发光材料BaAl2Si2O8∶Eu2+的物相结构与发光性能[J].无机化学学报,2008,24(6):994-997. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|