| 不同碳源对多孔球形LiFePO4/C复合材料的影响 |
| Effects of Carbon Sources on Properties of Porous LiFePO4/C Microsphere for Secondary Lithium Batteries |
|
| 摘要: 采用喷雾干燥-碳热还原法(SDCTM)，分别研究了无机和有机碳源对锂离子正极材料LiFePO4/C形貌、结构及其充放电性能的影响。结果表明：以无机碳源炭黑制备的LiFePO4/C呈不规则球形，一次颗粒粒径在800 nm左右，比表面积为2 m2·g-1， 0.1C放电比容量为107.3 mAh·g-1。而以有机碳源制备的LiFePO4/C，其形貌较为规则，呈多孔球形结构，具有较高的比表面积和放电比容量。其中，以柠檬酸为碳源制备的多孔球形LiFePO4/C复合材料，其孔径均在50 nm左右，比表面积可达32 m2·g-1；在室温下，0.1C和10C首次放电比容量分别为158.8和87.2 mAh·g-1，具有优异的循环性能和高倍率充放电性能。 |
| 关键词: LiFePO4/C 正极材料 多孔球形 喷雾干燥-碳热还原法(SDCTM) |
| 基金项目: |
| Abstract: Effects of carbon sources on porous LiFePO4/C microsphere were investigated by spray drying and carbothermal method(SDCTM). The results indicate that the defeatured porous LiFePO4/C microsphere obtained using carbon black as inorganic carbon source is with an average size of 800nm , small specific surface area of 2 m2·g-1 and a dischange capacing of 107.3 mAh·g-1 at 0.1C. However, the uniform porous LiFePO4/C microsphere was prepared using organic carbon sources. The regular porous LiFePO4/C microsphere has the average pore size of 50 nm and gives large specific surface area (32 m2·g-1) with citric acid. It presents large reversible capacity of 158.8 mAh·g-1 with 0.1C, even high rate capacity of 87.2 mAh·g-1 with 10C at room temperature. |
| Keywords: LiFePO4/C cathode material porous spherical spray drying and carbothermal method (SDCTM) |
| |
| 摘要点击次数: 1948 |
| 全文下载次数: 2086 |
| 于 锋,张敬杰,杨岩峰,宋广智.不同碳源对多孔球形LiFePO4/C复合材料的影响[J].无机化学学报,2009,25(1):42-46. |
| 查看全文 查看/发表评论 下载PDF阅读器 |