| 热诱导组装Ta2O5空心微球 |
| Temperature-triggered Assembly of Ta2O5 Hollow Microspheres |
|
| 摘要: 在有机体系中电化学溶解钽得到有机前驱体钽醇盐，在30 mL电解液中加入6 mL H2O2和0.6 g阳离子表面活性剂十六烷基三甲基溴化铵(CTAB)，150 ℃溶剂热反应24 h，产物经过高温热处理后得到Ta2O5空心微球。研究表明：溶剂热反应得到无定型Ta2O5纳米颗粒，600 ℃热处理后得到由纳米颗粒组装成的无定型Ta2O5半球 |
| 关键词: 有机电解合成 溶剂热 Ta2O5 空心球 |
| 基金项目: |
| Abstract: Amorphous Ta2O5 nanoparticles were solvothermally synthesized at 150 ℃ for 12 h in a mixed H2O2 and CTAB solution by using electrolyzed tantalum alkoxide as the starting material. The calcined samples were characterized by using X-ray diffraction(XRD) and scanning electron microscopy(SEM). The results show that amorphous Ta2O5 with hemispheres structure are obtained from nanoparticles after calcination at 600 ℃ for 5 h. Porous Ta2O5 microspheres are with an average diameter of 2 μm and a hollow cavity structure is self-assembled when subjecting to calcination at 900 ℃ for 5 h, the thickness of the hole is about 150 nm and the diameter of the hollow part is estimated to be 1.5 μm. However, the size of tantalum pentoxide is decreased after calcination at 600 ℃ and further decreased at 900 ℃ when anionic surfactant(oleic acid) is used instead of CTAB. The possible temperature-triggered microsphere assembly mechanism is discussed, and the abnormal phenomenon about the decreased tantalum pentoxide nano-particle is also reasonably interpreted. |
| Keywords: organic electrolysis solvothermal tantalum pentoxide hollow microsphere |
| |
| 摘要点击次数: 1318 |
| 全文下载次数: 1950 |
| 陈 颖,周幸福,刘 磊,范益群.热诱导组装Ta2O5空心微球[J].无机化学学报,2009,25(3):454-458. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|