| BaCe0.8-xNbxGd0.2O3-δ(0≤x≤0.45)的制备及性能研究 |
| Investigation into Preparation and Properties of BaCe0.8-xNbxGd0.2O3-δ(0≤x≤0.45) |
|
| 摘要: 采用高温固相反应法制备了质子导体BaCe0.8-xNbxGd0.2O3-δ(0≤x≤0.45)。结合XRD、SEM、EIS等技术对其物相、微观形貌、稳定性及电导率进行了研究。结果表明，在1 600 ℃烧结5 h制备的质子导体BaCe0.8-xNbxGd0.2O3-δ(0≤x≤0.45)均能保持主相为斜方晶的钙钛矿结构。Nb的加入可明显提高烧结样品的致密性及在CO2和水蒸气气氛下的稳定性。在湿润H2/Ar(0.4%，V/V)气氛中800 ℃下，x=0.1样品的电导率为5.73 mS·cm-1，电导活化能为0.35 eV，与x=0的样品相当。 |
| 关键词: 质子导体 BaCe0.8-xNbxGd0.2O3-δ 稳定性 电导率 |
| 基金项目: |
| Abstract: The proton conductors BaCe0.8-xNbxGd0.2O3-δ(0≤x≤0.45) were synthesized by high temperature solid-state reaction method and its phase, microstructure, stability and conductivity were studied by XRD, SEM and EIS. The results showed that the proton conductors BaCe0.8-xNbxGd0.2O3-δ(0≤x≤0.45) sintered at 1 600 ℃ for 5 h was orthorhombic perovskite structure. With x value increase, the density of samples increased and stability in the presence of H2O and CO2 was improved. The conductivity of sample with x=0.1 is 5.73 mS·cm-1 in wet H2/Ar(0.4%,V/V) at 800 ℃ and its conduction activation energy is 0.35 eV, which corresponds to that of sample with x=0. |
| Keywords: proton conductors BaCe0.8-xNbxGd0.2O3-δ stability conductivity |
| |
| 摘要点击次数: 1056 |
| 全文下载次数: 1673 |
| 王 岭,赵佳一,戴 磊,王 婧,李跃华,谢全安.BaCe0.8-xNbxGd0.2O3-δ(0≤x≤0.45)的制备及性能研究[J].无机化学学报,2010,26(4):701-707. |