| Ni/PdO/RuO2复合型活性阴极的制备与表征 |
| Preparation and Characterization of Ni/PdO/RuO2 Composite Active Cathode for Chlor-Alkali Industry |
|
| 摘要: 采用热分解氧化法，在Ni基体上制备以PdO为中间层、RuO2为活性层的Ni/PdO/RuO2复合型活性阴极，并通过XPS、XRD、能量色散X荧光(EDXRF)、SEM、极化曲线、循环伏安法和交流阻抗谱等表征其组成、结构与电化学性能。结果表明，Pd和Ru分别以PdO和RuO2的形式存在于Ni/PdO/RuO2复合型活性阴极中，其含量分别为1.25wt%和1.71wt%；在363 K、11 mol·L-1 NaOH溶液、3 kA·m-2电流密度下，Ni/PdO/RuO2复合型活性阴极的析氢过电位比Ni电极和Ni/RuO2电极分别低371和125 mV；循环伏安法循环72 h后，该复合型活性阴极双电层电容值减小30.6%，比Ni/RuO2电极表层结构更稳定；Ni/PdO/RuO2复合型活性阴极的表面粗糙度大且无明显的裂纹存在，与纯镍电极相比，该复合型活性阴极比表面积增加了31.12倍。 |
| 关键词: 氯碱工业 复合型活性阴极 热分解氧化法 析氢 |
| 基金项目: |
| Abstract: Ni/PdO/RuO2 and Ni/RuO2 composite active cathodes were prepared by thermal decomposition and oxidation method. The composition, structure and electrochemical performance of Ni/PdO/RuO2 composite active cathode, Ni/RuO2 active cathode and pure nickel cathode were investigated by XPS, XRD, Energy-dispersive X-Ray Fluorescence spectrometry (EDXRF), SEM, the polarization measurements, cyclic voltammetry and electrochemical impedance spectroscopy. It is found that Pd and Ru elements in the Ni/PdO/RuO2 composite cathode are mainly in the form of PdO and RuO2 and these two elements account for 1.25wt% and 1.71wt% respectively. The electrochemical results show that Ni/PdO/RuO2 composite cathode also exhibits high catalytic activity and stability. At the current density of 3 kA·m-2, hydrogen evolution overpotential of Ni/PdO/RuO2 composite active cathode is the lowest, which is about 125 mV lower than Ni/RuO2 active cathode and 371 mV lower than that of pure nickel in 11 mol·L-1 NaOH solution at 363 K. For active cathode treated by 72 h voltammetric cycles, the electric double layer capacitance of Ni/PdO/RuO2 composite active cathode decreases about 30.6%. The roughness of Ni/PdO/RuO2 composite active cathode is 32.12 times larger than that of the pure nickel cathode. Besides, there is no obvious cracked-mud. |
| Keywords: chlor-alkali industry composite active cathode thermal decomposition and oxidation hydrogen evolution |
| |
| 摘要点击次数: 1588 |
| 全文下载次数: 2253 |
| 王 雯,黎学明,杨文静,付银辉,李武林.Ni/PdO/RuO2复合型活性阴极的制备与表征[J].无机化学学报,2010,26(9):1633-1638. |