| CTAB辅助微波水热合成花簇状SnS微球 |
| Preparation of Flower-Like SnS Microsphere via CTAB Assisted Microwave Hydrothermal Synthesis |
|
| 摘要: 以氯化亚锡(SnCl2·2H2O)和硫代乙酰胺(TAA)为前驱物，十六烷基三甲基溴化铵(CTAB)为表面活性剂，采用微波水热法控制合成花簇状SnS微球。采用XRD和FESEM等分析手段对制备的样品进行表征。结果表明：合成的产物为正交晶系的SnS微晶，且结晶性良好；SnS微晶是由长方形纳米片自组装而成的花簇状微球。通过改变CTAB用量，可以实现花簇状SnS微晶的形貌和尺寸的调控，并初步分析了其形成过程。利用紫外-可见吸收光谱分析，产物的光学带隙约为1.51 eV；室温光致发光光谱表明，产物在832 nm处具有近红外发光特性。 |
| 关键词: SnS CTAB 微波水热 花簇状 光学性能 |
| 基金项目: |
| Abstract: Flower-like nanosheets clusters of SnS were synthesized by the reactions of SnCl2·2H2O and CH3CSNH2 in the presence of CTAB through a microwave hydrothermal process. XRD, FE-SEM were used to characterize the phase compositions and morphologies of as-prepared products. The results indicate that the as-prepared products are orthorhombic structure, The morphology of SnS powders have flower-like nanosheets clusters structure. The amount of CTAB plays an important role in controlling the shape and size of the products. A possible formation mechanism for the SnS with flower-like nanosheets clusters was discussed. UV-Visible spectral analysis shows that the optical band gap of the as-prepared products is about 1.51 eV. Photoluminescence spectrum measured at room temperature shows near-infrared emission at 832 nm. |
| Keywords: SnS CTAB microwave hydrothermal flower-like nanosheets clusters optical properties |
| |
| 摘要点击次数: 1523 |
| 全文下载次数: 2833 |
| 张培培,黄剑锋,曹丽云,辛 宇.CTAB辅助微波水热合成花簇状SnS微球[J].无机化学学报,2012,28(2):291-296. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|