| 阴离子改性甘油溶液中TiO2纳米管阵列的制备和表征 |
| Preparation and Characterization of TiO2 Nanotubes Array by Anodic Oxidation in Anionic Modified Glycerol-Based Electrolyte |
|
| 摘要: 本文采用电化学阳极氧化法以含氟的甘油和水混合溶液为电解液在纯钛表面制备了一层排列规整的TiO2纳米管阵列,研究了电解液中额外添加3种2价阴离子、不同的电解时间及不同的添加物浓度等因素对所获得的TiO2纳米管阵列形貌的影响。结果表明,在改性电解液中制备的TiO2纳米管阵列的长度均超过了未改性的电解液中制备的,并随着氧化时间的增长,纳米管管口直径增大,管壁变薄;同时添加的(NH4)2TiF6浓度在0.025～0.1 mol·L-1范围内均可获得管长更长且形貌较好的TiO2纳米管阵列。 |
| 关键词: TiO2纳米管阵列 阳极氧化 氟钛酸铵 |
| 基金项目: 国家自然科学基金(No.30970887,30600149),卫生部科学研究基金(No.WKJ2008-02-037),福建省杰青项目(No.2011J06019),教育部重点 项目(No.209061),福建省纳米材料重点实验室科学基金(No.NM10-03)资助项目。 |
| Abstract: High-order TiO2 nanotube arrays on titanium foils were prepared in glycerol-based electrolyte containing fluorine and water by electrochemical anodic oxidation in this work. The influence of different dianion additives, different oxidation duration and concentration of electrolyte additives on the effect of the morphology of TiO2 nanotube arrays were investigated. Results showed that the length of TiO2 nanotube arrays in the modified electrolyte were longer than the samples in the unmodified electrolyte. And with the growth of oxidation duration, the diameter of the nanotubes increased, the wall were thinner; moreover better and longer TiO2 nanotube arrays can be prepared in the glycerol-based electrolyte with the range of the concentration of (NH4)2TiF6. |
| Keywords: TiO2 nanotube arrays anodic oxidation fluorine titanate amines |
| 投稿时间：2012-04-23 修订日期：2012-07-31 |
| 摘要点击次数: 2415 |
| 全文下载次数: 2431 |
| 肖秀峰,梁建鹤,汤海贞,杨小娟,刘榕芳.阴离子改性甘油溶液中TiO2纳米管阵列的制备和表征[J].无机化学学报,2013,29(3):544-550. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|