| 表面预处理对镁铝水滑石结构性质和缓释性能影响 |
| Effects of Surface Pretreatment on Structure and Release Performances of Mg-Al Hydrotalcites |
|
| 摘要: 以Mg-Al-NO3水滑石（LDHs）为载体，将5-氟尿嘧啶（5-FU）通过离子交换法插入其层间，得5-FU/LDHs缓释材料。并对水滑石表面进行弱酸预处理改性，利用XRD、FTIR、TG-DSC、SEM和零电荷点（pHPZC）等表征手段，考察酸预处理对水滑石表面化学性质及微观结构的影响。结果表明，5-FU/LDHs的层间距从0.858 nm扩大到1.064 nm，层间5-FU2阴离子与主体层板通过氢键与静电作用，以呈一定角度单层交替排列于层间。酸预处理的水滑石粒径变小，层板正电荷密度增大。5-FU的释放机理是物理扩散、离子交换和药物溶解等协同作用，酸预处理可提高水滑石的缓释性能和稳定性。 |
| 关键词: 水滑石 5-氟尿嘧啶；插层；酸预处理；载体 |
| 基金项目: 湖南省自科基金重点项目（No.12JJ2008）；湖南省高校创新平台开放基金项目（No.12K048）；2012年湖南省大学生创新性实验计划资助项目。 |
| Abstract: The drug delivery materials (5-FU/LDHs) were obtained by intercalation of 5-Fluorouracil (5-FU) into the sheets of Mg-Al-NO3 hydrotalcites (LDHs) by ion-exchange method. The surface of the LDHs was modified with weak acid pretreatment. The influence of the acid-pretreatment on the surface chemical characteristics and microstructure of the LDHs was determined using X-ray diffractometry (XRD), Fourier transform-infrared spectrometer (FTIR), Thermo gravimetric and Differential scanning calorimeter(TG-DSC), Scanning electron microscopy (SEM) and point of zero charge (pHPZC). The results showed that the interlayer spaces of the 5-FU/LDHs were expanded from 0.858 to 1.064 nm. 5-FU2 anions were intercalated into the brucite sheets of the LDHs as a monolayer arranged alternately with a constant angle through hydrogen bonding and electrostatic attraction. Average particle size became smaller and permanent charge density of the sheets increased after the acid-pretreatment of the carrier. The release mechanism of the 5-FU was discussed. The in vitro releasing behavior of the 5-FU/LDHs materials was involved in physical diffusion, ions exchange and drug dissolution and so on. The release performances and thermostability could be improved after acid pretreatment. |
| Keywords: hydrotalcites 5-Fluorouracil intercalated acid pretreatment carrier |
| 投稿时间：2013-11-15 修订日期：2014-03-08 |
| 摘要点击次数: 1984 |
| 全文下载次数: 1834 |
| 黄清军,廖梦尘,曾虹燕,张伟,张治青,刘小军,李会.表面预处理对镁铝水滑石结构性质和缓释性能影响[J].无机化学学报,2014,30(7):1542-1548. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|