| 熔盐法制备氧化锆纳米棒 | |
| Preparation of Zirconia Nanorods by Molten Salt Method | |
| 摘要: 采用非水解溶胶-凝胶工艺合成氧化锆干凝胶粉，然后将干凝胶粉与熔盐混合制备氧化锆纳米棒。借助DTA-TG、XRD、FE-SEM、TEM等测试手段研究了氧化锆的物相转变过程，探讨了熔盐种类与用量、氟化物的添加等工艺参数对制备氧化锆纳米棒的影响。结果表明：以NaVO3为熔盐，用量为1：1（熔盐与干凝胶的质量比），并且在添加氟化钠的条件下能够制备产率高，且沿[010]方向择优生长的单斜氧化锆纳米棒；氟离子一方面加速了熔盐中Zr4+离子的传质，促使氧化锆干凝胶粉的溶解，另一方面吸附在氧化锆的高能晶面上抑制该晶面的生长，两者的共同作用促进了大量氧化锆纳米棒的形成。 | |
| 关键词: 氧化锆纳米棒 非水解溶胶-凝胶工艺 熔盐 氟化物 | |
| 基金项目: 国家自然科学基金（No.51662016，51362014）和江西省优势科技创新团队建设计划项目（No.20133BCB24010）资助。 | |
| Abstract: Zirconia nanorods were prepared via molten salt route, using zirconia dry gel powder as precursor synthesized by non-hydrolytic sol-gel (NHSG) method. Differential thermal analysis and thermogravimetric analysis (DTA-TG), X-ray diffraction analysis (XRD), transmission electron microscope (TEM) and field emission scanning electron microscopy (FE-SEM) were employed to characterize the phase transformation process of zirconia, the influences of the type, amount of molten salt and the role of fluoride on the formation of zirconia nanorods. The results show that the optimized molten salt type and dosage are NaVO3 and 1:1(mmolten salt:mxerogel mass ratio), respectively, and the monoclinic zirconia nanorods grow preferentially along the[010] direction in the presence of sodium fluoride. It is found that the F- in the flux plays a vital role in formation of zirconia nanorods:on one hand, the fluoride ions accelerate the mass transfer of Zr4+ ions and the dissolution of zirconia xerogel in molten salt system; on the other hand, fluoride ions adsorb on high-energy facets of the zirconia to block the growth along these facets. The interaction of two aspects promotes the formation of zirconia nanorods in large scale. | |
| Keywords: zirconia nanorods non-hydrolytic sol-gel process molten salt fluoride | |
| 投稿时间：2016-12-20 修订日期：2017-05-11 | |
| 摘要点击次数: 1538 | |
| 全文下载次数: 1090 | |
| 高啟蔚,江伟辉,刘健敏,冯果,陈婷,苗立锋.熔盐法制备氧化锆纳米棒[J].无机化学学报,2017,33(9):1555-1560. | |
| 查看全文 查看/发表评论 下载PDF阅读器 | |
| Support information: | |
|
| |
|
| |
|
| |