| 银纳米晶对铒镱共掺的TeO2-WO3-La2O3微晶玻璃发光性能的影响 |
| Influence of Silver Nanocrystals on the Luminescence Properties of Er3+/Yb3+ Co-doped TeO2-WO3-La2O3 Glass-Ceramics |
|
| 摘要: 通过熔融退火的方法以及热处理技术制备得到含有Er2WO6，La2WO6晶体的TeO2-WO3-La2O3-Er2O3-Yb2O3微晶玻璃，该玻璃具有优异的上转换发光性能。结果表明，在含银纳米晶的碲酸盐微晶玻璃中，银纳米晶和微晶的析出情况与银纳米晶的引入方式和热处理温度有关。经过390℃下15 min的热处理后，AgCl和AgNO3共掺的碲酸盐微晶玻璃比单掺AgCl或AgNO3的碲酸盐微晶玻璃具有更高的发光强度。银纳米晶与微晶的引入可协同提高碲酸盐玻璃的上转换发光性。 |
| 关键词: 碲酸盐微晶玻璃 硝酸银 氯化银 银纳米晶 表面等离子体共振 上转换 |
| 基金项目: 上海市科学技术委员会项目（No.12nm0504700）资助。 |
| Abstract: The transparent TeO2-WO3-La2O3-Er2O3-Yb2O3 glass-ceramics containing silver nanocrystals and micro-crystals such as Er2WO6, La2WO6 were prepared by the conventional melt-quenching method, which exhibit excellent up-conversion luminescence properties. The results show that the precipitation of silver nanocrystals and micro-crystals was related to the introducing way of silver nanocrystals and heat treatment temperature. After heat treated at 390℃ for 15 min, the luminescent intensity of the glass co-doped with AgCl and AgNO3 is higher than the glass which is single doped with AgCl or AgNO3. The introduction of silver nanocrystals and microcrystals can synergistically increase the UC luminescence of the tellurite glass. |
| Keywords: tellurite glass-ceramic sliver nitride sliver chloride silver nanocrystal LSPR up-conversion |
| 投稿时间：2018-01-09 修订日期：2018-04-19 |
| 摘要点击次数: 1235 |
| 全文下载次数: 545 |
| 陈淑文,林健,张文俊.银纳米晶对铒镱共掺的TeO2-WO3-La2O3微晶玻璃发光性能的影响[J].无机化学学报,2018,34(7):1341-1350. |