以开孔的二维MFI纳米片为构筑单元制备沸石片膜
Fabrication of Zeolite Membranes Using Two-Dimensional Open-Pore MFI Nanosheets as Building Blocks
作者单位E-mail
吴云琴 浙江师范大学先进催化材料教育部重点实验室, 金华 321004  
郑璐康 浙江师范大学先进催化材料教育部重点实验室, 金华 321004  
陈琦 浙江师范大学先进催化材料教育部重点实验室, 金华 321004  
俞梦婷 浙江师范大学先进催化材料教育部重点实验室, 金华 321004  
王金桂 齐鲁工业大学化学与制药工程学院, 济南 250353  
张富民 浙江师范大学先进催化材料教育部重点实验室, 金华 321004  
肖强 浙江师范大学先进催化材料教育部重点实验室, 金华 321004 xiaoq@zjnu.cn 
朱伟东 浙江师范大学先进催化材料教育部重点实验室, 金华 321004  
摘要: 以食人鱼溶液(体积比为3:1的95%~98%(w/w)H2SO4和30%(w/w)H2O2混合液)处理多层MFI(ML-MFI)除去有机结构导向剂(OSDA),经超声剥离和沉降纯化后得到了开孔的MFI沸石纳米片。采用X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、N2吸附-脱附、傅立叶变换红外光谱(FT-IR)和热重分析(TGA)等手段对得到的MFI沸石纳米片进行表征,发现食人鱼溶液处理可移除ML-MFI中的OSDA,再经超声剥离得到可分散、开孔的MFI沸石纳米片。将MFI沸石纳米片用简单抽滤的方式沉积到自制Al2O3载体上,不经二次生长得到了连续的沸石纳米片膜。单组分气体渗透性能测试结果表明,制备的MFI沸石纳米片膜对正/异丁烷的理想选择性为4.1~5.8,正丁烷的渗透速率为2.2×10-7~4.1×10-7 mol·m-2·s-1·Pa-1
关键词: 沸石    纳米结构  纳米片  食人鱼溶液  异构体分离
基金项目: 国家自然科学基金(No.21471131,21576243)和浙江省新苗人才计划资助项目(No.2017R404018)资助。
Abstract: Open-pore MFI zeolite nanosheets were prepared by removal of organic structure-directing agents (OSDA) from a multilamellar MFI zeolite (ML-MFI) using a mixture of 95%~98%(w/w) H2SO4 and 30%(w/w) H2O2 with VH2SO4:VH2O2=3:1 (known as piranha solution), followed by ultrasonication for exfoliation and sedimentation for purification. The exfoliated MFI zeolite nanosheets were characterized by various techniques, such as X-ray diffraction (XRD), scanning electron microscope (SEM), transmittance electron microscope (TEM), N2 adsorption-desorption, Fourier transform infrared spectrometer (FT-IR) and thermal gravimetric analyzer (TGA), etc., indicating that OSDA was removed after the piranha solution treatment and dispersed, open-pore MFI nanosheets were obtained followed by exfoliation through ultrasonication. Continuous MFI nanosheet membranes were prepared by depositing the open-pore MFI nanosheets on home-made alumina disc supports by a simple vacuum-assisted filtration method. Single gas permeance tests on the MFI zeolite nanosheet membranes indicated that ideal selectivities for n-butane over i-butane of 4.1~5.8 with a permeance of n-butane of 2.2×10-7~4.1×10-7 mol·m-2·s-1·Pa-1 were achieved.
Keywords: zeolites  membranes  nanostructures  nanosheets  piranha solution  isomer separation