| 片状Co9S8/ZnS/C复合材料的制备及电催化产氧性能 |
| Preparation and Electrocatalytic Performance of Flake Co9S8/ZnS/C Composites for Oxygen Evolution Reduction |
|
| 摘要: 以六水合硝酸钴[Co（NO3）2·6H2O]为钴源、六水合硝酸锌[Zn（NO3）2·6H2O]为锌源、2，2'-硫代二乙酸（C4H6O4S）为硫源，采用溶剂热法制备出了片状的Co9S8/ZnS/C复合材料。采用X射线衍射（XRD）、扫描电镜（SEM）、透射电镜（TEM）和N2吸附/脱附测试等手段对于片状Co9S8/ZnS/C复合材料结构和形貌等进行表征，同时对片状Co9S8/ZnS/C复合材料进行了电催化产氧性能测试。结果表明：片状Co9S8/ZnS/C复合材料的起始过电位为390 mV，塔菲尔斜率为144 mV·dec-1，具有高的电催化产氧性能。 |
| 关键词: Co9S8/C ZnS 过渡金属 电解水 析氧反应 溶剂热法 |
| 基金项目: 国家自然科学基金面上项目（No.21671092）、辽宁省"兴辽英才"科技创新领军人才项目（No.XLYC1802057）资助。 |
| Abstract: The flake Co9S8/ZnS/C composites were prepared by solvothermal method, through using cobalt hexahydrate[Co(NO3)2·6H2O] as cobalt source, zinc hexahydrate nitrate[Zn(NO3)2·6H2O] as zinc source and 2,2'-thiodiacetic acid (C4H6O4S) as sulfur source. The flake Co9S8/ZnS/C composites structure and morphology were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), N2 adsorption-desorption test. Meanwhile, the results of electrocatalytic oxygen evolution reaction for the flake Co9S8/ZnS/C composite showed that it had high electrocatalytic oxygen production performance, with the initial overpotential of 390 mV and the Tafel slope of 144 mV·dec-1. |
| Keywords: Co9S8/C ZnS transition metal water splitting oxygen evolution reaction solvothermal method |
| 投稿时间：2019-07-05 修订日期：2019-10-29 |
| 摘要点击次数: 1532 |
| 全文下载次数: 611 |
| 李志学,任铁强,耿忠兴,杨占旭.片状Co9S8/ZnS/C复合材料的制备及电催化产氧性能[J].无机化学学报,2019,35(12):2318-2322. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|