Mn、Mg共掺杂Ni(OH)2的电化学性能
Electrochemical Performance of Mn and Mg Co-doped Ni(OH)2
作者单位E-mail
姚寿广 江苏科技大学能源与动力学院, 镇江 212003 zjyaosg@126.com 
窦飞 江苏科技大学能源与动力学院, 镇江 212003
超威电源有限公司, 湖州 313100 
 
刘顿 江苏科技大学能源与动力学院, 镇江 212003
超威电源有限公司, 湖州 313100 
 
程杰 超威电源有限公司, 湖州 313100  
摘要: 采用缓冲溶液法制备复合掺杂Mn、Mg的正极材料Ni0.82Mn0.18-xMgx(OH)2(x=0.06、0.09、0.12)。采用XRD、XPS和SEM等测试表征材料的晶体结构、锰价态和形貌,采用循环伏安和恒流充放电测试研究Mn、Mg不同掺杂比例对氢氧化镍电化学性能的影响。结果表明,Mn、Mg掺杂样品均为β相,晶粒细化;Ni0.82Mn0.09Mg0.09(OH)2样品具有优异的电极反应可逆性和充放电性能,100 mA·g-1电流密度下的放电比容量(290.6 mAh·g-1)优于商用β-Ni(OH)2(281.1 mAh·g-1);且500 mA·g-1电流密度下循环30圈后,Ni0.82Mn0.09Mg0.09(OH)2的放电比容量未见衰减,其循环稳定性优于商用β-Ni(OH)2
关键词: 缓冲溶液法  掺杂  氢氧化镍  放电比容量  循环稳定性
基金项目: 国家自然科学基金(No.51776092)资助。
Abstract: To reduce costs and improve performance of the positive electrode materials, the buffer solution method was used to prepare manganese and magnesium doped nickel hydroxide, labeled as Ni0.82Mn0.18-xMgx(OH)2 (x=0.06, 0.09, 0.12). XRD, XPS and SEM tests were used to characterize the crystal structure, manganese valence state and morphology of the samples. Cyclic voltammetry and constant current charge-discharge tests were used to study the influence of Mn and Mg doping ratio on the electrochemical performance of Ni(OH)2. The results showed that the samples doped Mn and Mg were all β-phase and the crystal particles were smaller; Ni0.82Mn0.09Mg0.09(OH)2 showed excellent electrode reaction reversibility and charge-discharge performance. Specific discharge capacity (290.6 mAh·g-1) of Ni0.82Mn0.09Mg0.09(OH)2 was better than that of the commercial β-Ni(OH)2 (281.1 mAh·g-1) at 100 mA·g-1; moreover, after cycling for 30 cycles at a current density of 500 mA·g-1, the specific discharge capacity of Ni0.82Mn0.09Mg0.09(OH)2 was no decay, indicating its cycle stability is better than that of the commercial β-Ni(OH)2.
Keywords: buffer solution method  doping  nickel hydroxide  discharge capability  cyclic stability
投稿时间:2020-07-16 修订日期:2020-11-12
摘要点击次数:  143
全文下载次数:  118
姚寿广,窦飞,刘顿,程杰.Mn、Mg共掺杂Ni(OH)2的电化学性能[J].无机化学学报,2021,37(1):95-102.