| 表面活性剂辅助合成LiNi0.8Co0.1Mn0.1O2正极材料 |
| Surfactant-Assisted Synthesis of LiNi0.8Co0.1Mn0.1O2 Cathode Material |
|
| 摘要: 通过添加烷基季铵盐类表面活性剂来调控材料形貌和粒径的改性方法，在LiNi0.8Co0.1Mn0.1O2前驱体合成过程中添加表面活性剂十二烷基三甲基溴化铵（DTAB）和十六烷基三甲基溴化铵（CTAB），利用尿素作为配合剂和沉淀剂，采用溶剂热法合成LiNi0.8Co0.1Mn0.1O2前驱体。最后，高温混锂煅烧合成椭球形的空心多孔材料。相比于不添加表面活性剂的样本，改性的材料有着更小的粒径和更加规整的形貌。电化学测试表明，添加DTAB和CTAB之后，首次充电容量分别达到223与251 mAh·g-1（0.1C）。其中，添加CTAB的样品首次放电容量达到216 mAh·g-1（0.1C），100次循环后容量保持率为85.1%，高于LiNi0.8Co0.1Mn0.1O2的81.7%（0.1C）。表面活性剂的改性显著提高了材料的电化学性能，为高镍三元正极材料的改性提供了一种新的思路。 |
| 关键词: LiNi0.8Co0.1Mn0.1O2 表面活性剂 溶剂热法 前驱体 形貌 循环稳定性 |
| 基金项目: 陕西省自然科学基金（No.2018GY-166，2019TD-019，2019TSLGY04-01）、西安市自然科学基金（No.201805033YD11CG17（7））和西安市清洁能源重点实验室（No.2019219914SYS014CG036） |
| Abstract: Herein, a modification method was proposed to control the morphology and particle size of materials by adding alkyl quaternary ammonium salt surfactant. In the synthesis process of LiNi0.8Co0.1Mn0.1O2 precursor, the surfactant dodecyl trimethyl bromide (DTAB) and hexadecyl trimethyl bromide (CTAB) were added; the LiNi0.8Co0.1Mn0.1O2 precursor was synthesized by using urea as compounding agent and precipitation agent and the solvent heat method as the synthesis method. Finally, hollow porous materials with ellipsoidal shape were synthesized by high temperature calcination of mixed lithium. Compared with blank samples without surfactant, the materials modified by surfactant had smaller particle size and more regular morphology. Electrochemical test showed that the initial charging capacity reached 223 and 251 mAh·g-1 respectively after adding DTAB and CTAB. Among them, the initial discharge capacity of adding CTAB reached 216 mAh·g-1 (0.1C), and the capacity retention rate was 85.1% after 100 cycles, higher than 81.7% (0.1C) of LNCM811. The modification of surfactants significantly improves the electrochemical properties of the materials and provides a new perspective for the modification of high nickel ternary anode materials. |
| Keywords: LiNi0.8Co0.1Mn0.1O2 surfactant solvothermal method precursor morphology cycle stability |
| 投稿时间：2020-11-30 修订日期：2021-03-06 |
| 摘要点击次数: 1182 |
| 全文下载次数: 571 |
| 同佳欣,王娟,黄会星.表面活性剂辅助合成LiNi0.8Co0.1Mn0.1O2正极材料[J].无机化学学报,2021,37(5):835-843. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|