| Er3+掺杂Li2O-SrO-ZnO-Bi2O3玻璃中Er3+离子在1.53 μm处的荧光发射特性 |
| Luminescence Properties of Er3+ Ions in Er3+-Doped Li2O-SrO-ZnO-Bi2O3 Glasses with 1.53 μm Emission |
|
| 摘要: 采用传统的熔融法制备了Er3+掺杂的新型铋酸盐玻璃（Li2O-SrO-ZnO-Bi2O3，LSZB），并对其光谱性质进行了表征，分析了玻璃的拉曼光谱、吸收光谱、荧光光谱，利用Judd-Ofelt理论研究了其荧光特性。LSZB玻璃样品中Er3+的4I13/2→4I15/2跃迁发射峰位于1.53 μm处，半高宽约为78 nm。样品中Er3+的4I13/2能级寿命为2.848 ms，量子效率为99.93%，受激发射截面达到9.76×10-21 cm2。以上结果显示，Er3+掺杂LSZB玻璃有良好的光谱特性。 |
| 关键词: 铒 铋酸盐玻璃 光放大器 Judd-Ofelt理论 |
| 基金项目: 国家自然科学基金（No.21661036，21361028）资助。 |
| Abstract: Er3+-doped novel bismuthate (Li2O-SrO-ZnO-Bi2O3, LSZB) glasses have been fabricated through the conventional melt-quenching method, and the spectroscopic properties of Er3+ in the glasses were characterized. The density, refractive indexes, Raman spectra, optical absorption spectra, fluorescence spectra and radiative lifetime of the glasses were measured and analyzed. The fluorescence properties were calculated by using the Judd-Ofelt theory. The emission peak from the Er3+:4I13/2→4I15/2 transition located around 1.53 μm with a full width at half maximum (FWHM) of ~78 nm. The lifetime of the 4I13/2 level was 2.848 ms and the quantum efficiency was 99.93%, respectively. The emission cross section was estimated to be 9.76×10-21 cm2. In summary, the above results indicate that Er3+-doped LSZB glasses have good spectral characteristics. |
| Keywords: erbium bismuth glasses optical amplifier Judd-Ofelt theory |
| 投稿时间：2020-11-26 修订日期：2021-05-01 |
| 摘要点击次数: 827 |
| 全文下载次数: 456 |
| 张宁,林志文,满石清.Er3+掺杂Li2O-SrO-ZnO-Bi2O3玻璃中Er3+离子在1.53 μm处的荧光发射特性[J].无机化学学报,2021,37(6):984-988. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|