| 表面活性剂-模板化法制备多级孔β沸石及其四氢萘加氢裂化制苯、甲苯、二甲苯的催化性能 |
| Hierarchical β Zeolite by Surfactant-Templating Method: Preparation and Catalytic Performance in Tetralin Hydrocracking to Benzene, Toluene, and Xylene |
|
| 摘要: 采用表面活性剂-模板化法，分别以β-60和β-150为母体，选用十六烷基三甲基溴化铵(CTAB)作为表面活性剂，以一步和两步法制备了2种多级孔β沸石。以X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、N2吸附-脱附测试和NH3程序升温脱附(NH3-TPD)测试对多级孔β沸石的物化性质进行分析。采用等体积浸渍法负载25%的WO3制备成加氢裂化催化剂，考察其在四氢萘加氢裂化制备苯(B)、甲苯(T)和二甲苯(X)的催化性能。结果表明：相比于母体，一步制备样品的介孔孔容提高3倍以上，两步制备样品的介孔孔容提高1倍以上。另外，以β-60为母体，一步和两步制备样品的介孔均是无序的。一步制备样品的最高BTX收率是53%，两步制备样品的最高BTX收率是51%；然而，以β-150为母体，一步制备样品的介孔是无序的，而两步制备样品的介孔是有序的。一步制备样品的最高BTX收率是46%，两步制备样品的最高BTX收率是50%。因此，多级孔β沸石制备的加氢裂化催化剂的催化性能是由介孔的含量和有序度共同决定的。 |
| 关键词: β沸石 多级孔 表面活性剂 加氢裂化 |
| 基金项目: |
| Abstract: In this study, a series of hierarchical β zeolites were prepared from the parent zeolites (β-60 and β-150) by one/two-step surfactant-templating method with cetyltrimethylammonium bromide (CTAB) as the surfactant. The physicochemical properties of the hierarchical β zeolites were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), N2 adsorption-desorption test, and NH3 temperature-programmed desorption (NH3-TPD) test. The results show that the mesopore volume of the hierarchical β zeolites prepared in one step was increased by more than 3 times, and the mesopore volume of hierarchical β zeolites prepared in two steps was increased by more than 1 time compared with the parent zeolite. Furthermore, the hydrocracking catalysts were prepared by loading WO3 onto these hierarchical β zeolites, and their catalytic performance in the hydrocracking of tetralin to benzene (B), toluene (T), and xylene (X) was investigated. Taking β-60 as the parent zeolite, the mesopores of the hierarchically porous β zeolite obtained after one-step or two-step treatment were both disordered, and BTX yields reached 53% and 51%, respectively. However, taking β-150 as the parent zeolite, the mesopores of the hierarchical β zeolites prepared by the one-step method were disordered, while the mesopores of the samples prepared by the two-step method were ordered. The highest yield of BTX prepared by the one-step method was 46%, and that prepared by the two-step method was 50%. Therefore, the catalytic performance of hydrocracking catalyst prepared from hierarchical β zeolites was determined by the mesopore content and degree of order. |
| Keywords: β zeolite hierarchical surfactant hydrocracking |
| 投稿时间：2022-02-10 修订日期：2022-05-23 |
| 摘要点击次数: 595 |
| 全文下载次数: 285 |
| 张燕挺,党辉,张妮妮,陈胜利.表面活性剂-模板化法制备多级孔β沸石及其四氢萘加氢裂化制苯、甲苯、二甲苯的催化性能[J].无机化学学报,2022,38(7):1350-1360. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: 相关附件： 220057_Supporting_information (1).doc |
|
|
|
|
|
|