氢氧化镁的结晶习性研究
Study on the Growth of Magnesium Hydroxide Crystals
作者单位E-mail
向兰 清华大学化工系, 北京, 100084 xianglan@flotu.org 
金永成 清华大学化工系, 北京, 100084  
金涌 清华大学化工系, 北京, 100084  
摘要: 本文用负离子配位多面体模型探讨了NaOH水热介质中Mg(OH)2晶体的结晶习性,提出了Mg(OH)2的水热改性属溶解-结晶机制、生长基元为Mg(OH)64-八面体的观点.Mg(OH)2-NaOH-H2O体系高温热力学计算和电阻在线检测结果间接验证了生长基元论点.理论推导表明:Mg(OH)64-八面体的共棱连接方式决定了Mg(OH)2的结晶习性.
关键词: 氢氧化镁  晶体生长  水热改性
基金项目: 国家自然科学基金资助项目(No.50174532)
Abstract: The growth of Mg(OH)2 crystals in NaOH hydrothermal solution was studied by the theoretic model of anion coordination polyhedra of growth units. The experimental results and the theoretical analysis indicated that the hydrothermal modification of Mg(OH)2 was carried out via dissolution-crystallization route and octahedral Mg(OH)64- was the growth units of Mg(OH)2 crystals, which was supported further by the thermodynamic calculation results in Mg(OH)2-NaOH-H2O system at elevated temperature and the variation of electronic resistance of hydrothermal solution. The linkage of octahedral Mg(OH)64- in edge direction produced Mg(OH)2 crystals with the highest stability, which determined thefinal morphology of Mg(OH)2 crystals.
Keywords: magnesium hydroxide  growth of crystals  hydrothermal modification
投稿时间:2003-04-03 修订日期:2003-06-04
摘要点击次数:  10076
全文下载次数:  3609
向兰,金永成,金涌.氢氧化镁的结晶习性研究[J].无机化学学报,2003,19(8):837-842.
查看全文  查看/发表评论  下载PDF阅读器
Support information: