| 菲咯啉铜配位席夫碱基导电聚合物的制备和电化学性能 | |
| Preparation and electrochemical properties of phenanthroline copper coordination Schiff base conducting polymers | |
| 摘要: 以邻联甲苯胺和对苯二甲醛为原料制备席夫碱OTTP，并在席夫碱中掺杂不同比例的菲咯啉铜配合物，合成了菲咯啉铜配位席夫碱基导电聚合物[Cu(Phen)Cl2]X-OTTP(X为席夫碱与菲咯啉铜配合物的物质的量之比，X=1、0.8、0.6、0.4、0.2)。通过扫描电子显微镜、X射线衍射和傅里叶红外光谱等对产物的形貌结构等进行分析，通过循环伏安法、恒流充放电法和电化学阻抗谱分析了[Cu(Phen)Cl2]X-OTTP电极的电化学性能。表征结果表明席夫碱聚合物被不同比例的菲咯啉铜配合物掺杂后，形貌产生变化，片状的席夫碱表面产生很多孔隙，片状结构被破坏，基本单元结构的π-π堆积相互作用受影响，为电荷储存与电子交换提供丰富电活性位点。在 6 mol·L-1 KOH 电解质的三电极系统下，[Cu(Phen)Cl2]0.4-OTTP 在电流密度为 0.5 A·g-1时具有 278mAh·g-1的高比容量。混合装置超级电容电池[Cu(Phen)Cl2]0.4-OTTP//AC(AC为活性炭)在能量密度为26.16 Wh·kg-1时的功率密度为 276.99 W·kg-1。尤其是在 10 A·g-1的高电流密度下，混合装置经过 10 000 次恒流充放电循环后其比容量仍保留原始的97.13%。 | |
| 关键词: 席夫碱基聚合物 超级电容电池 电极材料 π-π堆积 | |
| 基金项目: 国家自然科学基金(No.51678059)、国土资源部退化及未利用土地整治工程重点实验室开放基金(No.SXDJ2017-1)、陕西省重点研发计划(No.2019GY-179)、陕西省土地整治重点实验室开放基金项目(No.2018-JC10)、中央高校基本科研业务费(No.300102298202)和延长石油集团科技计划项目(No.ycsy2020ky-A-1)资助。 | |
| Abstract: Preparation and electrochemical properties of Schiff base OTTP prepared from o-toluidine and p-benzaldehyde polymers doped with various proportions of phenanthroline copper complexes. The copper coordination polymer [Cu(Phen)Cl2]X-OTTP (X was the molar ratio of Schiff base to phenanthroline copper coordination complex, X=1, 0.8, 0.6, 0.4, 0.2) of Schiff base phenanthroline was synthesized by doping different proportions of phenanthroline copper complexes in Schiff base. The morphology and structure of the products were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR), and the electrochemical performance of the electrode materials [Cu(Phen)Cl2]X-OTTP were analyzed by cyclic voltammetry (CV), galvanostatic chargedischarge (GCD), and electrochemical impedance spectrum (EIS). The results exhibited that the morphology of the polymer Schiff base changed after doping with phenanthroline copper complexes. After doping, the Schiff base was scaly, with more holes on the surface and the layered structure was destroyed. The matrix π-π stacking was affected. In 6 mol·L-1 KOH electrolyte three-electrode system, [Cu(Phen)Cl2]0.4-OTTP had a high specific capacity of 278 mAh·g-1 at the current density of 0.5 A·g-1. The assembled supercapacitor [Cu(Phen)Cl2]0.4-OTTP//AC (AC=activated carbon) had a power density of 276.99 W·kg-1 at the energy density of 26.16 Wh·kg-1, and kept original specific capacity of 97.13% after 10 000 GCD cycles at current density of 10 A·g-1. | |
| Keywords: Schiff base polymer supercapattery electrode material π-π stacking | |