| 纳米CuFe2O4-rGO复合材料的制备及电化学性能 |
| Preparation and Electrochemical Properties of Nano CuFe2O4-rGO Composites |
|
| 摘要: 采用溶剂热法成功制备了纳米CuFe2O4-rGO复合材料。通过X射线衍射（XRD）、扫描电子显微镜（SEM）、透射电子显微镜（TEM）和电化学工作站对样品的结构、形貌及电容特性进行表征。结果表明，CuFe2O4纳米粒子均匀地分散在石墨烯片层间，其中CuFe2O4-20% rGO复合材料具有最优的电化学性能，当电流密度1 A·g-1时，其比电容为1 952.5 F·g-1，当电流密度为1 A·g-1时，CuFe2O4-20% rGO复合材料经1 000次充放电后的比电容保持率为86.17%。 |
| 关键词: 纳米CuFe2O4 石墨烯 电容特性 |
| 基金项目: 国家自然科学基金（No.51272239）资助项目 |
| Abstract: Nano CuFe2O4-rGO composites were successfully prepared by solvothermal method. The phase structure, morphology and capacitance of the sample were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical workstation, respectively. The results indicated that the CuFe2O4 nanoparticles were uniformly dispersed in the graphene nanosheets, and the CuFe2O4-20%rGO composite shown the best electrochemical performance. When the current density is 1 A·g-1 the specific capacitance of the CuFe2O4-20% rGO composite was 1 952.5 F·g-1, and shown an excellent cycling stability along with 86.17% specific capacitane retained after 1 000 cycle tests. |
| Keywords: nano CuFe2O4 grapheme capacitance |
| 投稿时间：2017-02-28 修订日期：2017-07-20 |
| 摘要点击次数: 1353 |
| 全文下载次数: 1105 |
| 段红珍,程霞,罗铭宇,周芳灵,李巧玲.纳米CuFe2O4-rGO复合材料的制备及电化学性能[J].无机化学学报,2017,33(12):2208-2214. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|